Síntese e caracterização de mulita utilizando sílica obtida da casca de arroz

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.creatorGonçalves, Gislayne Elisana-
Autor(es): dc.creatorSabioni, Antônio Claret Soares-
Autor(es): dc.creatorFerraz, Wilmar Barbosa-
Autor(es): dc.creatorCosta, Geraldo Magela da-
Autor(es): dc.creatorBrito, Walter de-
Autor(es): dc.creatorDias, José Alves-
Autor(es): dc.creatorGarcia, Fillipe Augusto da Costa-
Data de aceite: dc.date.accessioned2019-11-06T13:24:21Z-
Data de disponibilização: dc.date.available2019-11-06T13:24:21Z-
Data de envio: dc.date.issued2012-07-13-
Data de envio: dc.date.issued2012-07-13-
Data de envio: dc.date.issued2009-
Fonte completa do material: dc.identifierhttp://hdl.handle.net/123456789/1112-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/capes/554698-
Descrição: dc.descriptionMulita com composição 1,4 Al2O3.SiO2 foi sintetizada a partir de α-alumina comercial (Alfa Cesar Company) e de sílica obtida da calcinação da casca de arroz. Essa sílica possui alta área superficial, alta pureza e pequeno diâmetro médio de partícula. Pós de sílica e de alumina foram misturados na proporção estequiométrica 3Al2O3-2SiO2 correspondente a 71,8 % em peso de Al2O3 e 26,2 % em peso de SiO2, homogeneizados em moinho de disco orbital de alumina antes e após a calcinação a 1100ºC, durante 4 h, ao ar. Em seguida, os pós foram prensados uniaxialmente sob uma pressão de 1200 MPa. Os corpos verdes foram sinterizados a 1650ºC, por 4 h, ao ar. As densidades dos corpos sinterizados foram determinadas pelo método hidrostático. As caracterizações química e estrutural foram realizadas por ICP, DRX e MAS RMN de 29Si, respectivamente, e a análise microestrutural por MEV. Os resultados obtidos mostram que é possível sintetizar cerâmica mulita de alta pureza, com pouca fase vítrea, a partir da α-alumina e sílica, obtida da casca de arroz purificada e calcinada. ____________________________________________________________________________________________________-
Descrição: dc.descriptionAbstract: Mullite, composed of 1,4Al2O3.SiO2 was synthesized using commercial α- alumina (Alpha Cesar Company) and silica obtained from the calcinations of rice husk. This silica exhibits a high specific surface area, high purity and small average particle diameter. Silica (26.2 wt.%) and α-alumina powders (71.8 wt.%) were mixed and homogenized using an alumina orbital disc mill before and after the calcinations at 1100ºC for 4 h in an air atmosphere. Then, the powders were pressed uniaxially at a pressure of 1200 MPa. The green compacts were sintered at 1650ºC, for 4 h, in air. The density of compacted sintering samples was determined using the hydrostatic method. The chemical and structural properties were observed using ICP (Inductively Coupled Plasma), XRD (X-ray diffraction) and 29Si MAS (Magic Angle Spinning) NMR (Nuclear Magnetic Resonance) and the microstructural characterization performed using SEM (Scanning Electron Micrography). The results show that it is possible to synthesize mullite ceramic of high-purity and with little glassy phase from the α-alumina and silica obtained from the rice husk that is purified and calcinated.-
Idioma: dc.languagept_BR-
Direitos: dc.rightsAutorização concedida ao Repositório Institucional da UFOP pela Revista Escola de Minas em 12/09/2013 para depositar uma cópia eletrônica dos artigos publicados por esse periódico em que ao menos um dos autores é aluno ou professor da UFOP.-
Palavras-chave: dc.subjectMulita-
Palavras-chave: dc.subject3Al2O3.2SiO2-
Palavras-chave: dc.subjectCasca de arroz-
Palavras-chave: dc.subjectMullite-
Palavras-chave: dc.subject3Al2O3.2SiO2-
Palavras-chave: dc.subjectRice husk-
Título: dc.titleSíntese e caracterização de mulita utilizando sílica obtida da casca de arroz-
Título: dc.titleSynthesis and characterization of mullite using silica from rice husk-