Viabilidade do uso de argilas cauliníticas do Quadrilátero Ferrífero para a indústria cerâmica

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.creatorSánchez, Miguel Genaro Peralta-
Autor(es): dc.creatorCarrera, Ana Mercedes Morales-
Autor(es): dc.creatorVarajão, Angélica Fortes Drummond Chicarino-
Autor(es): dc.creatorFerreira, Mônica Martiniano-
Data de aceite: dc.date.accessioned2019-11-06T13:24:17Z-
Data de disponibilização: dc.date.available2019-11-06T13:24:17Z-
Data de envio: dc.date.issued2012-07-11-
Data de envio: dc.date.issued2012-07-11-
Data de envio: dc.date.issued2011-
Fonte completa do material: dc.identifierhttp://hdl.handle.net/123456789/1071-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/capes/554677-
Descrição: dc.descriptionSete amostras compostas, representativas de três ocorrências de argila caulinítica do Quadrilátero Ferrífero, foram caracterizadas física, mineralógica e quimicamente visando seu uso na indústria cerâmica. Apesar da presença predominante de caulinita, variações nos teores de Fe2O3 entre 2 a 44%, refl etidos pela presença de goethita e hematita, acarretam diferentes cores que variam entre branco (ACM e DB), amarelo (R5), vermelho amarelado (FS) e vermelho (DV, R1 e AM). Corpos cerâmicos foram queimados a 900 e 1100 °C, sendo que as cores praticamente não mudaram após a queima. Entretanto, somente corpos feitos com DV e R1 cumpriram as especifi cações técnicas para cerâmica, não apresentando fraturas e atingindo altas resistências à compressão: 96,2 MPa e 64,2 MPa, respectivamente. Para as outras amostras foram testadas misturas com fi lito (F) nas proporções de 5, 10, 15, 20 e 25% e queima a 900 e 1100 °C. Os melhores resultados dos corpos cerâmicos, com ausência de fraturas, resistências à compressão entre 69,15 e 29,6 MPa e que cumpriram as especifi cações técnicas, foram obtidos nas proporções: ACM+15F, DB+5F, R5+5F, FS+5F, AM+5F e queima a 900 ºC. ____________________________________________________________________________________________________-
Descrição: dc.descriptionAbstract: Seven samples from three kaolin deposits of the Quadrilátero Ferrífero were characterized by physical, mineralogical and chemical analyses in order to determine their use in the ceramic industry. Despite the predominant presence of kaolinite, the variations in the Fe2O3 content from 2 to 44%, due to presence of goethite and hematite, resulted in different colors, namely: white (ACM and DB), yellow (R5), yellowed red (FS) and red (DV, R1 and AM). Specimens were burned at 900 and 1100 °C and they almost didn’t change color. However, only specimens made with DV and R1 samples reached the technical specifi cations for the ceramic industry, without fractures and with values of compression strength of 96.2 and 64.2 MPa, respectively. The other samples were made by mixing phyllite in the proportions of 5, 10, 15, 20 and 25% and burned at 900 and 1100 °C. The bricks made with ACM+15F, DB+5F, R5+5F, FS+5F, AM+5F and burned at 900 ºC reached the technical specifi cations for ceramic industry, without fractures and with values of compression strength between 69.15 and 29.6 MPa.-
Idioma: dc.languagept_BR-
Publicador: dc.publisherCerâmica-
Direitos: dc.rightsO Periódico Cerâmica permite que o Repositório Institucional da Universidade Federal de Ouro Preto (UFOP) deposite uma cópia eletrônica dos artigos publicados por esse periódico em que ao menos um dos autores faça parte da comunidade cientifica da UFOP. Fonte: Licença concedida mediante preenchimento de formulário enviado no dia 20/02/2014.-
Palavras-chave: dc.subjectCerâmica-
Palavras-chave: dc.subjectQuadrilátero Ferrífero (MG)-
Palavras-chave: dc.subjectCaulim-
Palavras-chave: dc.subjectFilito-
Palavras-chave: dc.subjectCeramic industry-
Palavras-chave: dc.subjectKaolin-
Palavras-chave: dc.subjectPhyllite-
Título: dc.titleViabilidade do uso de argilas cauliníticas do Quadrilátero Ferrífero para a indústria cerâmica-
Título: dc.titleAvailability of the kaolin from Quadrilátero Ferrífero for the ceramic industry-