Microstructural characterization of bainitic steel submitted to torsion testing and interrupted accelerated cooling

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.creatorCota, André Barros-
Autor(es): dc.creatorSantos, Dagoberto Brandão-
Data de aceite: dc.date.accessioned2019-11-06T13:24:11Z-
Data de disponibilização: dc.date.available2019-11-06T13:24:11Z-
Data de envio: dc.date.issued2012-07-05-
Data de envio: dc.date.issued2012-07-05-
Data de envio: dc.date.issued2000-
Fonte completa do material: dc.identifierhttp://hdl.handle.net/123456789/992-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/capes/554641-
Descrição: dc.descriptionHSLA low-carbon bainitic steel containing B was submitted to torsion tests to simulate controlled rolling, followed by interrupted accelerated cooling. Microstructural characteristics and the mechanisms for the refinement of structure were evaluated using light microscopy, scanning electron microscopy, transmission electron microscopy, and Vickers hardness testing. The final microstructure was found to contain complex mixture of granular bainite, small islands of MA constituent, bainitic ferrite, and polygonal ferrite. Increasing the cooling rate or decreasing the finish cooling temperature resulted in a decrease in the volume fraction and average size of the MA islands and the polygonal ferrite. A finish cooling temperature of 400 8 C produced a microstructure consisting of fine laths of bainitic ferrite with an interlath MA constituent. A quantitative relationship between the accelerated cooling variables and the ferrite grain size was developed.-
Idioma: dc.languageen-
Direitos: dc.rightsO Periódico Materials Characterization concede permissão para depósito do artigo no Repositório Institucional da UFOP. Número da licença: 3345930428979.-
Título: dc.titleMicrostructural characterization of bainitic steel submitted to torsion testing and interrupted accelerated cooling-