Ativação alcalina da escória de aciaria.

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.contributorSilva, Guilherme Jorge Brigolini-
Autor(es): dc.contributorOliveira, Víctor de Andrade Alvarenga-
Autor(es): dc.contributorSilva, Guilherme Jorge Brigolini-
Autor(es): dc.contributorOliveira, Víctor de Andrade Alvarenga-
Autor(es): dc.contributorGama, João Luiz Calmon Nogueira da-
Autor(es): dc.contributorSantos, White José dos-
Autor(es): dc.contributorBorges, Paulo Henrique Ribeiro-
Autor(es): dc.creatorBorba Júnior, José Carlos-
Data de aceite: dc.date.accessioned2025-08-21T15:43:49Z-
Data de disponibilização: dc.date.available2025-08-21T15:43:49Z-
Data de envio: dc.date.issued2023-11-19-
Data de envio: dc.date.issued2023-11-19-
Data de envio: dc.date.issued2022-
Fonte completa do material: dc.identifierhttp://www.repositorio.ufop.br/jspui/handle/123456789/17820-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/capes/1022713-
Descrição: dc.descriptionPrograma de Pós-Graduação em Engenharia Civil. Departamento de Engenharia Civil, Escola de Minas, Universidade Federal de Ouro Preto.-
Descrição: dc.descriptionA demanda da humanidade por bens e serviços tem causado aumento na busca por produtos muito acima do crescimento da população. Nesse sentido, há a necessidade de diminuir o impacto causado pelas indústrias de bens de consumo. Esse trabalho propõe o uso de uma escória de aciaria como matéria prima para a produção de um cimento alcalinamente ativado, que pode vir a ser um substituto do cimento Portland. Para isso, o trabalho iniciou com uma extensa revisão bibliográfica sistematizada sobre o assunto que mostrou lacunas de conhecimento a serem exploradas. Assim, o trabalho propõe a dosagem de pastas de escória de aciaria de forno a arco elétrico, comparando os resultados de resistência à compressão pelos métodos de uma parte e de duas partes. Os traços feitos pelo método de duas partes alcançaram as maiores resistências à compressão, chegando a 15 MPa aos 90 dias, enquanto que os traços de uma parte só atingiram 4 MPa. Também foi feita a caracterização dos produtos de hidratação aos 28 e 90 dias de idade, através das técnicas de microscopia eletrônica de varredura, análise termogravimétrica e difratometria de raios X com tratamento de dados pelo Rietveld. Os resultados mostram a evolução das pastas hidratadas, com formação de silicato de cálcio hidratado e o aluminato de cálcio hidratado. As quantidades de cada produto hidratado obtidas pelos dois métodos convergiram, apresentando menos que 10 % de diferença calculada.-
Descrição: dc.descriptionThe humanity's demand for products and services has caused an increase in the search for products far above population growth. In this sense, there is a need to reduce the impact caused by consumer industries. This work proposes the use of steel slag as a raw material for the production of an alkaline activated cement, which could be a substitute for Portland cement. To this end, the work began with an extensive systematic bibliographic review on the subject that showed gaps in knowledge to be explored. Thus, the work proposes the dosage of electric arc furnace steel slag pastes, comparing the results of compressive strength by the one-part and two-part methods. The mixes made using the two-part method achieved the highest compressive strengths, reaching 15 MPa at 90 days, while the one-part mixes only reached 4 MPa. The hydration products were also characterized at 28 and 90 days of age, using scanning electron microscopy, thermogravimetric analysis and X-ray diffractometry techniques with data processing by Rietveld. The results show the evolution of hydrated pastes, with the formation of hydrated calcium silicate and hydrated calcium aluminate. The quantities of each hydrated product obtained by the two methods converged, showing less than a 10% calculated difference.-
Formato: dc.formatapplication/pdf-
Idioma: dc.languagept_BR-
Direitos: dc.rightsaberto-
Direitos: dc.rightshttp://creativecommons.org/licenses/by-nc-nd/3.0/us/-
Direitos: dc.rightsAutorização concedida ao Repositório Institucional da UFOP pelo(a) autor(a) em 01/11/2023 com as seguintes condições: disponível sob Licença Creative Commons 4.0 que permite copiar, distribuir e transmitir o trabalho, desde que sejam citados o autor e o licenciante. Não permite o uso para fins comerciais nem a adaptação.-
Palavras-chave: dc.subjectCimento-
Palavras-chave: dc.subjectCimento - aglomerantes álcali-ativados-
Palavras-chave: dc.subjectCimento - ativação alcalina-
Palavras-chave: dc.subjectEscória - metalurgia - aciaria-
Palavras-chave: dc.subjectEscória - metalurgia-
Título: dc.titleAtivação alcalina da escória de aciaria.-
Tipo de arquivo: dc.typelivro digital-
Aparece nas coleções:Repositório Institucional - UFOP

Não existem arquivos associados a este item.