Tijolo prensado produzido com rejeito de barragem de minério de ferro.

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.contributorSilva, Guilherme Jorge Brigolini-
Autor(es): dc.contributorBorba Júnior, José Carlos-
Autor(es): dc.contributorSilva, Guilherme Jorge Brigolini-
Autor(es): dc.contributorBorba Júnior, José Carlos-
Autor(es): dc.contributorPereira, Mariana Arruda-
Autor(es): dc.contributorSantos, White José dos-
Autor(es): dc.creatorFaria, Andréia da Conceição de-
Data de aceite: dc.date.accessioned2025-08-21T15:22:41Z-
Data de disponibilização: dc.date.available2025-08-21T15:22:41Z-
Data de envio: dc.date.issued2023-05-31-
Data de envio: dc.date.issued2023-05-31-
Data de envio: dc.date.issued2022-
Fonte completa do material: dc.identifierhttp://www.repositorio.ufop.br/jspui/handle/123456789/16745-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/capes/1012470-
Descrição: dc.descriptionPrograma de Pós-Graduação em Engenharia das Construções. Departamento de Engenharia Civil, Escola de Minas, Universidade Federal de Ouro Preto.-
Descrição: dc.descriptionA Construção civil é umas das áreas que mais consomem matéria prima no mundo, contribuindo para a degradação ambiental. Diversos estudos têm sido realizados para torná-la mais sustentável, e o reaproveitamento de resíduos da mineração, tem sido incentivado. O rejeito de minério de ferro é um coproduto da mineração, gerado em grandes volumes no estado de Minas Gerais. Esses rejeitos são geralmente depositados em barragens que, quando mal executadas, podem trazer riscos conhecidos à população, como no desastre de Mariana. Esse trabalho propõe uma aplicação para esse rejeito, desenvolvendo um estudo de dosagens que podem ser utilizados na produção de tijolos prensados. Para a estabilização dos tijolos, se propõe a ativação alcalina com hidróxido de sódio e silicato de sódio, desenvolvendo 12 traços contendo o rejeito de minério de ferro como matéria prima principal. A partir destes materiais, foi definida uma metodologia para a produção de protótipos, que representem os tijolos. Os protótipos foram caracterizados, e ensaiados quanto à resistência à compressão e absorção de água. A partir destes ensaios três traços apresentaram resultados satisfatórios, com resistência a compressão entre 13,15 MPa a 19,51 MPa aos 7 dias, e absorção de água com valores entre 9,52% e 10,24 %, sendo comprovado que este material pode ser utilizado na produção de tijolos prensados para a construção civil.-
Descrição: dc.descriptionCivil construction is one of the areas that most consume raw materials in the world, contributing to environmental degradation. Several studies have been carried out to make it more sustainable, and the reuse of mining waste has been encouraged. Iron ore tailings are a co-product of mining, generated in large volumes in the state of Minas Gerais. These tailings are usually deposited in dams that, when poorly executed, can pose known risks to the population, as in the Mariana disaster. This work proposes an application for this waste, developing a study of dosages that can be used in the production of pressed bricks. For the stabilization of the bricks, alkaline activation with sodium hydroxide and sodium silicate is proposed, developing 12 traces containing iron ore waste as the main raw material. From these materials, a methodology was defined for the production of prototypes that represent the bricks. The prototypes were characterized and tested for compressive strength and water absorption. From these tests, three traits showed satisfactory results, with compressive strength between 13.15 MPa and 19.51 MPa after 7 days, and water absorption with values between 9.52% and 10.24%, proving that this material can be used in the production of pressed bricks for civil construction.-
Formato: dc.formatapplication/pdf-
Idioma: dc.languagept_BR-
Direitos: dc.rightsaberto-
Direitos: dc.rightshttp://creativecommons.org/licenses/by-nd/3.0/us/-
Direitos: dc.rightsAutorização concedida ao Repositório Institucional da UFOP pelo(a) autor(a) em 24/05/2023 com as seguintes condições: disponível sob Licença Creative Commons 4.0 que permite copiar, distribuir e transmitir o trabalho, desde que sejam citados o autor e o licenciante. Não permite a adaptação.-
Palavras-chave: dc.subjectBarragens de rejeitos - minérios de ferro-
Palavras-chave: dc.subjectTijolos - tijolo prensado-
Título: dc.titleTijolo prensado produzido com rejeito de barragem de minério de ferro.-