Produção e avaliação de painéis de partícula com resina alternativa de polietileno tereftalato e breu colofônia

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.contributorAkasaki, Jorge Luís-
Autor(es): dc.contributorUniversidade Estadual Paulista (UNESP)-
Autor(es): dc.contributorSilva, Sérgio Augusto Mello da-
Autor(es): dc.creatorBispo, Rodrigo Andraus-
Data de aceite: dc.date.accessioned2025-08-21T17:36:31Z-
Data de disponibilização: dc.date.available2025-08-21T17:36:31Z-
Data de envio: dc.date.issued2025-08-20-
Data de envio: dc.date.issued2025-08-01-
Fonte completa do material: dc.identifierhttps://hdl.handle.net/11449/313027-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/11449/313027-
Descrição: dc.descriptionO polietileno tereftalato (PET) é um polímero da família do poliéster que se tornou amplamente difundido quando utilizado na produção de garrafas de refrigerantes e água potável. O descarte inadequado desse material e a falta de alternativas de reuso são problemas significativos que geram poluição e contribuem para o acúmulo de plástico nos oceanos. O objetivo deste trabalho foi produzir e avaliar painéis de partículas homogêneos feitos de madeira de pinus – conhecida por sua baixa densidade e rápido crescimento – aglomerados com adesivo alternativo de polietileno tereftalato reciclado (PETr) e breu colofônia, com potencial para aplicação na construção civil e indústria moveleira. Para produção dos painéis, o polímero reciclado e a resina foram moídos até atingirem diâmetro médio de partícula inferior a 250 µm, contribuindo para o aumento da superfície específica e auxiliando o processo de fusão e adesão às partículas de madeira. A madeira de pinus foi caracterizada quanto a densidade e geometria das partículas. As partículas foram homogeneizadas e prensadas para consolidar os painéis sob temperatura e pressão controladas (T = 160°C, P = 5,7MPa). Três níveis de adesivo alternativo foram propostos (10%, 20% e 30%) em relação à massa seca de pinus, com diferentes teores de mistura entre PETr e breu (100% - 0%, 75% - 25%, 50% - 50%, 25% - 75% e 0% - 100%). Os painéis produzidos foram avaliados quanto às propriedades físicas de densidade (D), teor de umidade (U), inchamento em espessura após 24 horas (I), absorção de água (AA) e absorção superficial (AS) bem como propriedades mecânicas, incluindo módulo de resistência à flexão estática (MOR), módulo de elasticidade (MOE) e resistência à tração perpendicular (TP), além de propriedades morfológicas avaliadas por microscopia eletrônica de varredura (MEV) e microscopia óptica (MO). Os resultados indicaram que os painéis das composições C230 e C330 atenderam aos requisitos mínimos estabelecidos pelas normas brasileira ABNT NBR 14810-2 (2024), americanas ANSI A208.1 (2022) e CS 236-66 (1996) e europeia EN 312 (2010), apresentando uma alternativa com menor impacto ambiental em relação aos painéis atualmente em uso.-
Descrição: dc.descriptionPolyethylene terephthalate (PET) is a polymer from the polyester family that has become widely used in the production of soft drink and potable water bottles. The improper disposal of this material and the lack of reuse alternatives are significant issues that cause pollution and contribute to the accumulation of plastic in the oceans. The objective of this study was to produce and evaluate homogeneous particleboards made from pine wood - known for its low density and fast growth - bonded with an alternative adhesive composed of recycled polyethylene terephthalate (PETr) and colophony rosin, with potential applications in civil construction and the furniture industry. For the production of the panels, the recycled polymer and the rosin were ground until reaching an average particle diameter of less than 250 µm, increasing the specific surface area and aiding the fusion and adhesion process to the wood particles. The pine wood was characterized in terms of particle density and geometry. The particles were homogenized and pressed to consolidate the panels under controlled temperature and pressure conditions (T = 160 °C, P = 5,7 MPa). Three levels of alternative adhesive were proposed (10%, 20%, and 30%) relative to the dry mass of pine, with different mixing ratios of PETr and rosin (100%-0%, 75%-25%, 50%-50%, 25%-75%, and 0%-100%). The produced panels were evaluated for physical properties including density (D), moisture content (U), thickness swelling after 24 hours (I), water absorption (WA), and surface absorption (SA), as well as mechanical properties such as modulus of rupture (MOR), modulus of elasticity (MOE), and internal bond strength (IB). Morphological properties were also assessed using scanning electron microscopy (SEM) and optical microscopy (OM). The results indicated that the produced panels of the C230 and C330 compositions met the minimum requirements established by the Brazilian standard ABNT NBR 14810-2 (2024), the American standards ANSI A208.1 (2022) and CS 236-66 (1996), and the European standard EN 312 (2010), offering an environmentally friendlier alternative compared to conventional particleboards currently in use.-
Descrição: dc.descriptionCoordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)-
Descrição: dc.descriptionCAPES: 88887.817701/2023-00-
Descrição: dc.descriptionCAPES: 001-
Formato: dc.formatapplication/pdf-
Formato: dc.formatapplication/pdf-
Idioma: dc.languagept_BR-
Publicador: dc.publisherUniversidade Estadual Paulista (UNESP)-
Direitos: dc.rightsinfo:eu-repo/semantics/restrictedAccess-
Palavras-chave: dc.subjectPainel de partículas-
Palavras-chave: dc.subjectPolietileno tereftalato-
Palavras-chave: dc.subjectBreu colofônia-
Palavras-chave: dc.subjectMadeira de pinus-
Palavras-chave: dc.subjectPropriedades físico-mecânicas-
Palavras-chave: dc.subjectParticleboards-
Palavras-chave: dc.subjectPolyethylene terephthalate-
Palavras-chave: dc.subjectColophony rosin-
Palavras-chave: dc.subjectPine wood-
Palavras-chave: dc.subjectPhysicalmechanical properties-
Título: dc.titleProdução e avaliação de painéis de partícula com resina alternativa de polietileno tereftalato e breu colofônia-
Título: dc.titleProduction and evaluation of particleboards with alternative polyethylene terephthalate and rosin resin-