Influência da espessura de restaurações indiretas na passagem de energia e na microdureza após a cimentação, utilizando a resina composta pré-aquecida como agente cimentante

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.contributorBresciani, Eduardo-
Autor(es): dc.contributorUniversidade Estadual Paulista (UNESP)-
Autor(es): dc.contributorSouza, Luana dos Santos-
Autor(es): dc.creatorMonnerat, Maria Fernanda Luiz-
Data de aceite: dc.date.accessioned2025-08-21T20:20:19Z-
Data de disponibilização: dc.date.available2025-08-21T20:20:19Z-
Data de envio: dc.date.issued2025-01-23-
Data de envio: dc.date.issued2025-01-23-
Data de envio: dc.date.issued2024-12-12-
Fonte completa do material: dc.identifierhttps://hdl.handle.net/11449/259941-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/11449/259941-
Descrição: dc.descriptionEste trabalho tem como o objetivo avaliar a influência da espessura das restaurações indiretas de resina composta na passagem de luz e na microdureza da periferia e do centro do agente cimentante, quando cimentadas com a resina composta pré-aquecida, utilizando um fotopolimerizador monowave e outro polywave. Material e Métodos: Foram confeccionados 60 discos de resina composta, 10 de cada grupo, nas espessuras de 1,5, 2,5 e 3,5mm. Fotopolimerizadores monowave ou polywave foram utilizados para as análises antes e após a cimentação com a resina pré-aquecida. As amostras foram submetidas ao teste de irradiância, feito com um espectrorradiômetro com esfera de integração (MSC15 - Gigahertz Optik GmbG), antes da cimentação, e um teste de microdureza Knoop (KHN), utilizando um microdurômetro (FM-700; Future-Tech CorpTokyo, Japan), na camada de cimento obtida. Resultados: O teste Anova detectou diferenças estatísticas. Para a irradiância, as espessuras foram significativamente diferentes (Tukey, p < 0,001), com o grupo de 1,5 mm apresentando maior passagem de luz em comparação aos outros, que diminuem à medida que a espessura do material restaurador aumenta. Quanto à microdureza, diferenças estatísticas foram encontradas somente no fator espessura (p < 0,001), diminuindo os valores de dureza à medida que a espessura aumentava. Para as regiões, a periferia foi superior ao centro somente com o polywave. Conclusão: A espessura das restaurações afeta a passagem de luz e a microdureza da resina pré-aquecida, com espessuras menores favorecendo uma maior irradiância, e consequentemente maiores valores de dureza da resina composta.-
Descrição: dc.descriptionObjective: This study aims to evaluate the influence of the thickness of indirect composite resin restorations on light transmission and microhardness of the cementing agent at the periphery and center when cemented with preheated composite resin, using a monowave and a polywave light curing unit. Materials and Methods: A total of 60 composite resin discs were fabricated, 10 for each group, with thicknesses of 1.5, 2.5, and 3.5 mm, and were light-cured using either the monowave or polywave device. These samples were evaluated before and after cementation with the preheated composite resin. The samples underwent an irradiance test, performed with a spectroradiometer with an integrating sphere (MSC15 - Gigahertz Optik GmbH), and a Knoop microhardness (KHN) test, using a microhardness tester (FM-700; FutureTech Corp, Tokyo, Japan). Results: The ANOVA test detected statistical differences for irradiance, with the thicknesses showing significant differences (Tukey, p < 0.001). The 1.5 mm group showed the highest light transmission compared to the others, with light transmission decreasing as the thickness of the restorative material increased. Regarding microhardness, statistical differences were found only for the thickness factor (p < 0.001), with hardness values decreasing as thickness increased. As for the regions, significant differences (p = 0.015) were found between the center and periphery, with the periphery showing higher hardness values. Conclusion: The thickness of the restorations affects light transmission and microhardness of the preheated resin, with thinner restorations favoring higher irradiance and, consequently, higher composite resin hardness values-
Formato: dc.formatapplication/pdf-
Idioma: dc.languagept_BR-
Publicador: dc.publisherUniversidade Estadual Paulista (UNESP)-
Direitos: dc.rightsinfo:eu-repo/semantics/restrictedAccess-
Palavras-chave: dc.subjectCimentação-
Palavras-chave: dc.subjectCura luminosa de adesivos dentários-
Palavras-chave: dc.subjectResina composta-
Palavras-chave: dc.subjectCementation-
Palavras-chave: dc.subjectLight-curing of dental adhesives-
Palavras-chave: dc.subjectComposite resins-
Título: dc.titleInfluência da espessura de restaurações indiretas na passagem de energia e na microdureza após a cimentação, utilizando a resina composta pré-aquecida como agente cimentante-
Título: dc.titleInfluence of indirect restorations thickness on energy transmission and microhardness at the cementation interface, using preheated composite resin as a cementing agent-