Efeito do pH na alteração volumétrica de materiais biocerâmicos: análise em microtomografia computadorizada

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.contributorTanomaru Filho, Mario-
Autor(es): dc.creatorMendonça, Giovanna da Cunha-
Data de aceite: dc.date.accessioned2025-08-21T15:33:25Z-
Data de disponibilização: dc.date.available2025-08-21T15:33:25Z-
Data de envio: dc.date.issued2024-01-16-
Data de envio: dc.date.issued2024-01-16-
Data de envio: dc.date.issued2023-11-28-
Fonte completa do material: dc.identifierhttps://hdl.handle.net/11449/252815-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/11449/252815-
Descrição: dc.descriptionpH ácido pode ocorrer na região periradicular e afetar propriedades de materiais biocerâmicos reparadores. O objetivo deste estudo foi avaliar o efeito do pH na alteração volumétrica do biocerâmico pronto para uso NeoPUTTY (NP, Nusmile, EUA) e pó/líquido MTA Repair HP (MTAHP, Angelus, Brasil), após imersão em PBS (pH 7.35) ou ácido butírico (AB, pH 4.1) por 7 dias. Dentes bovinos extraídos foram utilizados para confecção de tubos de dentina com 4 mm de comprimento, 1.5 mm de diâmetro e espessura de parede de aproximadamente 1 mm. Os tubos de dentina foram preenchidos (n=5): NP/PBS, NP/AB, MTAHP/PBS, MTAHP/AB; e mantidos em estufa a 37ºC por 24 horas. Escaneamento inicial em microtomografia computadorizada (micro-CT; SkyScan 1176, Bruker, Kontich, Bélgica) com tamanho de voxel 8.74 µm foi realizado. Posteriormente, os espécimes foram imersos em 1.5 mL de PBS ou ácido butírico (n=5) e mantidos em estufa a 37 ºC por 7 dias. Após esse período, novos escaneamentos em micro-CT foram conduzidos. Porcentagem de alteração volumétrica (extremidade ou parte interna) dos materiais foi determinada. Os dados foram submetidos aos testes estatísticos ANOVA e Tukey e teste Kruskal-Wallis (α=5%). Todos os materiais apresentaram perda volumétrica quando imersos em PBS ou ácido butírico nas extremidades em contato com as soluções. Porém, MTAHP/AB apresentou maior perda volumétrica (P<0.05). Não houve diferença estatística na alteração volumétrica para avaliação da parte interna (P>0.05). NP em ambos os meios de imersão, e MTAHP quando imerso em PBS apresentaram estabilidade volumétrica, com valores inferiores a 1%. Conclui-se que pH ácido promove perda volumétrica para o cimento de silicato de cálcio pó-líquido MTAHP.-
Descrição: dc.descriptionAn acidic pH in the periradicular tissues may affect properties of repair bioceramic materials. This study evaluated the effect of pH on the volumetric change of the ready-to-use bioceramic NeoPUTTY (NP, Nusmile, USA) compared to the powder/liquid cement MTA Repair HP (MTAHP, Angelus, Brazil), after immersion in PBS (pH 7.35) or butyric acid (BA, pH 4.1) for 7 days. Extracted bovine teeth were used to manufacture dentine tubes with a length of 4 mm, an internal diameter of 1.5 mm and a 1mm dentine thickness. The dentine tubes were filled (n=5): NP/PBS, NP/BA, MTAHP/PBS, MTAHP/BA; and kept in an oven at 37 ºC for 24 hours. Initial scanning in micro-computed tomography (micro-CT; SkyScan 1176, Bruker, Kontich, Belgium) with a voxel size of 8.74 µm was performed. Then, the specimens were immersed in 1.5 mL of PBS or butyric acid (n = 5) and kept in an oven at 37°C for 7 days. After this period, new micro-CT scans were performed. Percentage of volumetric change (extremity or internal part) of the materials was assessed. ANOVA/Tukey and Kruskal-Wallis tests were performed (α=5%). All materials showed a decrease in volume after immersion in PBS or butyric acid at the extremities in contact with the solutions. However, MTAHP/BA showed the highest volumetric loss (p<0.05). There was no difference on the volumetric change when the internal part of the materials was evaluated (p>0.05). NP in both solutions and MTAHP when immersed in PBS showed volumetric stability, with values below 1%. The acidic pH provided greater volumetric decrease for calcium silicate-based MTAHP.-
Descrição: dc.descriptionConselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)-
Descrição: dc.descriptionPIBIC: 136623/2020-4-
Formato: dc.formatapplication/pdf-
Idioma: dc.languagept_BR-
Publicador: dc.publisherUniversidade Estadual Paulista (UNESP)-
Direitos: dc.rightsinfo:eu-repo/semantics/restrictedAccess-
Palavras-chave: dc.subjectCalcarea silicata-
Palavras-chave: dc.subjectEndodontia-
Palavras-chave: dc.subjectMicrotomografia por raio-X-
Palavras-chave: dc.subjectCalcarea silicata-
Palavras-chave: dc.subjectEndodontics-
Palavras-chave: dc.subjectX-Ray microtomography-
Título: dc.titleEfeito do pH na alteração volumétrica de materiais biocerâmicos: análise em microtomografia computadorizada-
Título: dc.titleEffect of pH on the volumetric change of bioceramic materials: a micro-computed tomographic analysis-