Avaliação do efeito do recobrimento dos biovidros biok e 45S5 na superfície de implantes de zircônia: estudo in vivo e in vitro

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.contributorde Vasconcellos, Luana Marotta Reis-
Autor(es): dc.contributorCampos, Tiago Moreira Bastos-
Autor(es): dc.contributorUniversidade Estadual Paulista (UNESP)-
Autor(es): dc.creatorAvelino, Sarah de Oliveira Marco-
Data de aceite: dc.date.accessioned2025-08-21T18:16:49Z-
Data de disponibilização: dc.date.available2025-08-21T18:16:49Z-
Data de envio: dc.date.issued2023-01-17-
Data de envio: dc.date.issued2023-01-17-
Data de envio: dc.date.issued2022-11-16-
Fonte completa do material: dc.identifierhttp://hdl.handle.net/11449/238808-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/11449/238808-
Descrição: dc.descriptionO estudo avaliou o efeito do recobrimento de biovidros 45S5 e bioK na superfície de implantes de zircônia na osteogênese in vitro e na osseointegração in vivo. Para isso, foram confeccionadas amostras de zircônia T (Tosho, Japão) que foram divididas em 3 grupos: zircônia polida (Z); zircônia recoberta com biovidro 45S5 (45); zircônia recoberta com biovidro biok (bk). As amostras produzidas para os testes de caracterização e etapa in vitro mediram 6,0 x 4,0 mm, enquanto que para a etapa in vivo apresentaram 2,5x 2,5mm de altura. Após a produção, a morfologia das superfícies das amostras foi analisada por microscopia eletrônica de varredura (MEV) e estas foram submetidas ao teste de rugosidade média (Ra). Posteriormente à caracterização, as amostras foram submetidas aos testes biológicos in vitro e in vivo. Na etapa in vitro células mesenquimais obtidas de fêmures de ratos foram isoladas e plaqueadas com as amostras visando avaliar a influência destas na morfologia, atividade e diferenciação celular de osteoblastos, utilizando os testes biológicos de citotoxicidade, avaliação do conteúdo de proteína total, atividade da fosfatase alcalina e formação de nódulos de mineralização. Na etapa in vivo 18 ratos foram submetidos à cirurgia para colocação dos implantes nas tíbias direitas e esquerdas, os quais receberam implantes do mesmo material, conforme os grupos descritos acima. Os animais foram eutanasiados após 4 semanas do procedimento cirúrgico. As tíbias direitas foram submetidas à análise histológica e histomorfométrica, enquanto as tíbias esquerdas foram submetidas ao teste de push out. Com os resultados in vitro pudemos observar que os grupos experimentais não foram citotóxicos, propiciaram um ambiente adequado à atividade e diferenciação celular, e ainda permitiram o espraiamento celular sobre as amostras. Não foram observadas diferenças estatisticamente significantes entre os grupos experimentais nas análises in vivo. Concluiu-se que os recobrimentos nos implantes de zircônia com os biovidros 45S5 e biok foram produzidos adequadamente e permitiram a atividade e diferenciação celular, bem como neoformação óssea ao redor dos implantes. Novos estudos devem ser realizados para fornecer informações adicionais sobre o comportamento do recobrimento dos biovidros na superfície de implantes de zircônia.-
Descrição: dc.descriptionThe study evaluated the effect of bio-glass 45S5 and bioK coating on zirconia implant surfaces on in vitro osteogenesis and in vivo osseointegration. For this purpose, zirconia T (Tosho, Japan) samples were made and divided into 3 groups: polished zirconia (Z); zirconia coated with bioglass 45S5 (45); zirconia coated with biok (bk). The samples produced for the characterization tests and in vitro stage measured 6.0 x 4.0 mm, while for the in vivo stage they were 2.5x 2.5 mm in height. After production, the surface morphology of the samples was analyzed by scanning electron microscopy (SEM) and they were submitted to the average roughness test (Ra). After characterization, the samples were submitted to in vitro and in vivo biological tests. In the in vitro stage mesenchymal cells obtained from rat femurs were isolated and plated with the samples to evaluate their influence on osteoblast morphology, activity and cell differentiation, using the biological tests of cytotoxicity, total protein content, alkaline phosphatase activity and mineralization nodule formation. In the in vivo stage 18 rats underwent surgery to place the implants in the right and left tibiae, which received implants of the same material, according to the groups described above. The animals were euthanized 4 weeks after the surgical procedure. The right tibiae were subjected to histological and histomorphometric analysis, while the left tibiae were subjected to the push out test. With the in vitro results we could observe that the experimental groups were not cytotoxic, provided an adequate environment for cell activity and differentiation, and also allowed cell spreading over the samples. No statistically significant differences were observed between the experimental groups in the in vivo analyses. It was concluded that the coatings on zirconia implants with 45S5 and biok bioglass were adequately produced and allowed cell activity and differentiation, as well as bone neoformation around the implants. Further studies should be carried out to provide additional information on the coating behavior of bio glasses on the surface of zirconia implants.-
Descrição: dc.descriptionCoordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)-
Formato: dc.formatapplication/pdf-
Formato: dc.formatapplication/pdf-
Idioma: dc.languagept_BR-
Publicador: dc.publisherUniversidade Estadual Paulista (UNESP)-
Direitos: dc.rightsinfo:eu-repo/semantics/openAccess-
Palavras-chave: dc.subjectosteogênese-
Palavras-chave: dc.subjectosseointegração-
Palavras-chave: dc.subjectzircônia-
Palavras-chave: dc.subjectbiovidro-
Palavras-chave: dc.subjectosteogenesis-
Palavras-chave: dc.subjectosseointegration-
Palavras-chave: dc.subjectzirconia-
Palavras-chave: dc.subjectbioglass-
Título: dc.titleAvaliação do efeito do recobrimento dos biovidros biok e 45S5 na superfície de implantes de zircônia: estudo in vivo e in vitro-
Título: dc.titleEvaluation of the effect of coating biok and 45S5 bioglasses on the surface of zirconia implants: in vitro an in vivo study-
Tipo de arquivo: dc.typelivro digital-
Aparece nas coleções:Repositório Institucional - Unesp

Não existem arquivos associados a este item.