Structural and microstructural properties of Si-C and Si-C-B powders obtained by high-energy ball milling

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.contributorInstituto de Ciência e Tecnologia-
Autor(es): dc.contributorInstituto de Pesquisa e Desenvolvimento-
Autor(es): dc.contributorUniversidade Estadual Paulista (UNESP)-
Autor(es): dc.contributorInstituto de Química-
Autor(es): dc.creatorFerreira, L. M.-
Autor(es): dc.creatorMégda, D. S.-
Autor(es): dc.creatorde Souza, A. C.-
Autor(es): dc.creatorMarques, R. F.C. [UNESP]-
Autor(es): dc.creatorRamos, E. C.T.-
Autor(es): dc.creatorChad, V. M.-
Autor(es): dc.creatorRamos, A. S.-
Data de aceite: dc.date.accessioned2022-08-04T22:05:52Z-
Data de disponibilização: dc.date.available2022-08-04T22:05:52Z-
Data de envio: dc.date.issued2022-04-28-
Data de envio: dc.date.issued2022-04-28-
Data de envio: dc.date.issued2016-01-01-
Fonte completa do material: dc.identifierhttp://dx.doi.org/10.4028/www.scientific.net/MSF.869.19-
Fonte completa do material: dc.identifierhttp://hdl.handle.net/11449/220693-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/11449/220693-
Descrição: dc.descriptionThis work evaluated on the structural modification during high-energy ball milling of the Si-50C, Si-42.9C-19.1B e Si-33.3C-44.4B (at.-%) powder mixtures from elemental powders. Electron images revealed on occurrence of continuous fracture mechanisms in brittle particles during their processing, which presented rounded particles lower than 10 μm. X-ray diffraction results of Si-50C powders indicated that the intensity of Si peaks was slightly reduced after milling for 17 h, which were moved to the direction of larger diffraction angles after 7 h of milling, suggesting that carbon atoms were dissolved into the Si lattice in order to form an extended solid solution. Following, these values were increased due to the discrete exothermic formation of the SiC compound. In Si-C-B powder mixtures, the SiC and B4C compounds were formed after milling for 7 h.-
Descrição: dc.descriptionUniversidade Federal de Alfenas Instituto de Ciência e Tecnologia, Rodovia José Aurélio Vilela 11999-
Descrição: dc.descriptionUniversidade do Vale do Paraíba Instituto de Pesquisa e Desenvolvimento, Avenida Shishima Hifumi 2911, Urbanova-
Descrição: dc.descriptionUniversidade Estadual Paulista Instituto de Química, Rua Prof. Francisco Degni, 55, Quitandinha-
Descrição: dc.descriptionUniversidade Federal do Mato Grosso Instituto de Química, Rua Prof. Francisco Degni, 55, Quitandinha-
Descrição: dc.descriptionUniversidade Estadual Paulista Instituto de Química, Rua Prof. Francisco Degni, 55, Quitandinha-
Formato: dc.format19-24-
Idioma: dc.languageen-
Relação: dc.relationMaterials Science Forum-
???dc.source???: dc.sourceScopus-
Palavras-chave: dc.subjectCarbides-
Palavras-chave: dc.subjectHigh-energy ball milling-
Palavras-chave: dc.subjectPhase transformation-
Título: dc.titleStructural and microstructural properties of Si-C and Si-C-B powders obtained by high-energy ball milling-
Aparece nas coleções:Repositório Institucional - Unesp

Não existem arquivos associados a este item.