Atenção: Todas as denúncias são sigilosas e sua identidade será preservada.
Os campos nome e e-mail são de preenchimento opcional
Metadados | Descrição | Idioma |
---|---|---|
Autor(es): dc.contributor | Universidade de São Paulo (USP) | - |
Autor(es): dc.contributor | Universidade Estadual Paulista (Unesp) | - |
Autor(es): dc.creator | Giarola, J. M. | - |
Autor(es): dc.creator | Calderón-Hernández, J. W. | - |
Autor(es): dc.creator | Conde, F. F. | - |
Autor(es): dc.creator | Marcomini, J. B. | - |
Autor(es): dc.creator | de Melo, H. G. | - |
Autor(es): dc.creator | Avila, J. A. [UNESP] | - |
Autor(es): dc.creator | Bose Filho, W. W. | - |
Data de aceite: dc.date.accessioned | 2022-02-22T00:46:21Z | - |
Data de disponibilização: dc.date.available | 2022-02-22T00:46:21Z | - |
Data de envio: dc.date.issued | 2021-06-25 | - |
Data de envio: dc.date.issued | 2021-06-25 | - |
Data de envio: dc.date.issued | 2020-12-31 | - |
Fonte completa do material: dc.identifier | http://dx.doi.org/10.1007/s11665-021-05640-4 | - |
Fonte completa do material: dc.identifier | http://hdl.handle.net/11449/206175 | - |
Fonte: dc.identifier.uri | http://educapes.capes.gov.br/handle/11449/206175 | - |
Descrição: dc.description | Friction stir welding (FSW) is an excellent alternative process used in pipelines circumferential welds due to fusion welded joint low corrosion resistance. This study describes the corrosion resistance as a function of the microstructural features resulting from an API X70 FSW welded joint. The microstructural features were examined by optical microscopy, scanning electron microscopy, and x-ray diffraction. The corrosion analysis was conducted employing potentiodynamic polarization tests using an electrochemical microcell, which allowed to test small circular areas delimited by a 2 mm in diameter O-ring gasket. The base metal and heat-affected zone were the most susceptible regions to corrosion due to their banded microstructures. The re-stirred-zone and stir zone were the most resistant regions to corrosion which was associated to grain refinement. The corrosion rate presented by the base metal and the heat-affected zone was approximately six times higher than the region of least susceptibility to corrosion, in this case, the re-stirred-zone. | - |
Descrição: dc.description | Department of Materials Engineering University of São Paulo (USP), Av. Trabalhador São Carlense 400 | - |
Descrição: dc.description | Department of Metallurgical and Materials Engineering University of São Paulo (USP), Av. Professor Mello Moraes, 2463 - Butantã | - |
Descrição: dc.description | São Paulo State University (UNESP), Campus of São João da Boa Vista | - |
Descrição: dc.description | São Paulo State University (UNESP), Campus of São João da Boa Vista | - |
Idioma: dc.language | en | - |
Relação: dc.relation | Journal of Materials Engineering and Performance | - |
???dc.source???: dc.source | Scopus | - |
Palavras-chave: dc.subject | API 5L X70 | - |
Palavras-chave: dc.subject | corrosion rate | - |
Palavras-chave: dc.subject | corrosion resistance | - |
Palavras-chave: dc.subject | electrochemical microcell | - |
Palavras-chave: dc.subject | friction stir welding | - |
Palavras-chave: dc.subject | potentiodynamic polarization tests | - |
Título: dc.title | Corrosion Behavior and Microstructural Characterization of Friction Stir Welded API X70 Steel | - |
Tipo de arquivo: dc.type | livro digital | - |
Aparece nas coleções: | Repositório Institucional - Unesp |
O Portal eduCAPES é oferecido ao usuário, condicionado à aceitação dos termos, condições e avisos contidos aqui e sem modificações. A CAPES poderá modificar o conteúdo ou formato deste site ou acabar com a sua operação ou suas ferramentas a seu critério único e sem aviso prévio. Ao acessar este portal, você, usuário pessoa física ou jurídica, se declara compreender e aceitar as condições aqui estabelecidas, da seguinte forma: