Autor(es): dc.contributor | Universidade Estadual Paulista (Unesp) | - |
Autor(es): dc.creator | Figueredo, Rodrigo Monzon | - |
Autor(es): dc.creator | de Oliveira, Mariana Cristina | - |
Autor(es): dc.creator | de Paula, Leandro Jesus | - |
Autor(es): dc.creator | Acciari, Heloisa Andréa | - |
Autor(es): dc.creator | Codaro, Eduardo Norberto | - |
Data de aceite: dc.date.accessioned | 2022-02-22T00:25:12Z | - |
Data de disponibilização: dc.date.available | 2022-02-22T00:25:12Z | - |
Data de envio: dc.date.issued | 2020-12-11 | - |
Data de envio: dc.date.issued | 2020-12-11 | - |
Data de envio: dc.date.issued | 2019-01-01 | - |
Fonte completa do material: dc.identifier | http://dx.doi.org/10.1016/j.jmrt.2018.08.015 | - |
Fonte completa do material: dc.identifier | http://hdl.handle.net/11449/198668 | - |
Fonte: dc.identifier.uri | http://educapes.capes.gov.br/handle/11449/198668 | - |
Descrição: dc.description | Susceptibility to hydrogen-induced cracking of API 5L B and X52MS low-carbon steels inNACE 177-A, 177-B and 284-B solutions has been investigated by the present work. A met-allographic analysis of these steels was performed before and after NACE TM0284 standardtesting. Corrosion products were characterized by scanning electron microscopy and X-raydispersive energy spectrometry, which were subsequently identified by X-ray diffraction.Thus it was found that pH directly affects the solubility of corrosion products and hydrogenpermeation. Both steels showed generalized corrosion in solution 177-A, and a discontin-uous film was formed on their surfaces in solution 177-B, however, only the API 5L B steelfailed the HIC test and exhibited greater crack length ratio in solution 177-A. In solution284-B whose pH is higher, the steels exhibited thick mackinawite films with no internalcracking. | - |
Descrição: dc.description | São Paulo State University (UNESP), School of Engineering, Guaratinguetá, SP, Brazil | - |
Idioma: dc.language | en | - |
Relação: dc.relation | Journal of Materials Research and Technology | - |
???dc.source???: dc.source | Scopus | - |
Palavras-chave: dc.subject | Hydrogen embrittlement | - |
Palavras-chave: dc.subject | Hydrogen sulfide | - |
Palavras-chave: dc.subject | Hydrogen-induced cracking | - |
Palavras-chave: dc.subject | Low carbon steel | - |
Palavras-chave: dc.subject | Sour corrosion | - |
Título: dc.title | A comparative study of hydrogen-induced crackingresistances of API 5L B and X52MS carbon steels | - |
Tipo de arquivo: dc.type | livro digital | - |
Aparece nas coleções: | Repositório Institucional - Unesp |
O Portal eduCAPES é oferecido ao usuário, condicionado à aceitação dos termos, condições e avisos contidos aqui e sem modificações. A CAPES poderá modificar o conteúdo ou formato deste site ou acabar com a sua operação ou suas ferramentas a seu critério único e sem aviso prévio. Ao acessar este portal, você, usuário pessoa física ou jurídica, se declara compreender e aceitar as condições aqui estabelecidas, da seguinte forma: